Okujwayelekile: ASTM B196M-2003/B197M-2001

●Izici nezinhlelo zokusebenza:

I-C17300 i-beryllium yethusi inokusebenza okuhle kakhulu okubandayo nokusebenza okuhle kokushisayo.I-C17300 beryllium yethusi isetshenziswa kakhulu njenge-diaphragm, i-diaphragm, i-bellows, intwasahlobo.Futhi inezici zokungabi nanhlansi, futhi inokusebenza okuhle kokusika

●Ukwakheka kwekhemikhali:

Ithusi + isici esicacisiwe u-Cu: ≥99.50

I-Nickel+Cobalt Ni+Co: ≤0.6 (lapho i-Ni+Co≮0.20)

IBeryllium Yiba: 1.8 ~ 2.0

Ukuhola Pb: 0.20 ~ 0.60

I-Beryllium yethusi iyisisombululo esiqinile esine-supersaturated esinengxube yethusi.I-alloy engeyona i-ferrous enenhlanganisela enhle yezakhiwo zemishini, izakhiwo ezibonakalayo, izakhiwo zamakhemikhali kanye nokumelana nokugqwala.Ngemuva kwesixazululo esiqinile nokwelashwa kokuguga, inomkhawulo wamandla aphezulu, ukuqina nokunwebeka.Umkhawulo, umkhawulo wesivuno kanye nomkhawulo wokukhathala, futhi ngesikhathi esifanayo une-conductivity ephezulu kagesi, ukuguquguquka okushisayo, ubulukhuni obuphezulu nokumelana nokugqoka, ukumelana nokukhuphuka okuphezulu nokumelana nokugqwala, okusetshenziselwa kabanzi ekwenzeni izinto ezihlukahlukene zokufaka isikhunta, esikhundleni sokukhiqizwa kwensimbi High- ukunemba, isikhunta esimise okuyinkimbinkimbi, okokusebenza kwe-electrode yokushisela, imishini yokukhipha umjovo, izibhakela zomshini wokubumba umjovo, umsebenzi ongagugi futhi omelana nokugqwala, njll. Itheyiphu yethusi ye-Berryllium isetshenziswa kumabhulashi emoto encane, omakhalekhukhwini, amabhethri, kanye nemikhiqizo. , futhi iyimpahla yezimboni ebaluleke kakhulu futhi ebalulekile ekwakheni umnotho kazwelonke.

Imingcele ejwayelekile ye-beryllium yethusi:

Ukuminyana 8.3g/cm3

Ukuqina ngaphambi kokucisha i-200-250HV

Ukuqina ngemva kokucisha≥36-42HRC

Ukucisha izinga lokushisa ngu-315℃≈600℉

Isikhathi sokupheka amahora ama-2

Izinga lokushisa lokuthambisa lingu-930 ℃

Ukuqina ngemva kokuthambisa kungu-135±35HV

Amandla okuqina≥1000mPa

Amandla esivuno (0.2%) MPa: 1035

I-Elastic Modulus (GPa): 128

I-Conductivity≥18%IACS

I-Thermal conductivity≥105w/m.k20℃